Material for the production of components and tool inserts with conformal cooling in the area of injection moulding and die-casting as well as functional parts.
Materials
Hot-work steel (maraging steel)
Range of application
Technical data after recommended heat treatment
|
1 Tensile test according to DIN EN ISO 50125. 2 By using a special heat treatment a higher elongation can be achieved. 3 Preliminary values subject to change or update. 4 Hardness test according to DIN EN ISO 6508. |
|
| Yield Point Re1 | 1.550 N/mm2 |
| Tensile Strength Rm1 | 1650 N/mm2 |
| Elongation A 1,2 | 2 - 3 % |
| Young's modulus 3 | approx. 200 · 103 N/mm2 |
| Thermal conductivity λ3 | approx. 20 Wm/k |
| Hardness 4 | up to 52 HRC |
Heat treatment
Heat up with 100 °C/h up to 540 °C. Maintain temperature for 6-10 hours. Allow the components to cool down in the oven with 100 °C/h.
Chemical Composition
COMPONENT INDICATIVE VALUE (%)
Fe Balance
C 0 –0,03
Si 0 –0,10
Mn 0 –0,15
P 0 –0,010
S 0 –0,010
Cr 0 –0,25
Mo 4,50 – 5,20
Ni 17,0 – 19,0
Ti 0,80 – 1,20
Co 8,50 – 10,0